Opaque white coating composition comprising essentially cellulose ester/cross-linking agent/catalyst/solvent and organic liquid

ABSTRACT

A COATING COMPOSITION AND METHOD OF OBTAINING SAME BY MIXING AN ORGANIC SOLVENT WHICH CONTAINS AT LEAST 85% BY VOLUME PARAFFINIC HYDROCARBONS AND HAS A BOILING POINT OF AT LEAST ABOUT 3000*F. WITH A CROSS-LINKABLE RESIN LACQUER. AN OPAQUE WHITE COATING IS OBTAINED BY APPLYING THE COMPOSITION TO A SUBSTRATE AND CURING SAME THEREON.

United States Patent OPAQUE WHITE COATING COMPOSITION COM- PRISING ESSENTIALLY CELLULOSE ESTER/ CROSS-LINKING AGENT/CATALYST/SOLVENT AND ORGANIC LIQUID Ehrlich M. Eiland, Lower Burrell, Pa., assignor to Aluminum Company of America, Pittsburgh, Pa.

No Drawing. Original application Dec. 6, 1968, Ser. No. 781,977, now abandoned. Divided and this application Aug. 9, 1971, Ser. No. 170,369

Int. Cl. C08b 21/14; C08g 37/32; C08j 1/26 U.S. Cl. 260-14 3 Claims ABSTRACT OF THE DISCLOSURE A coating composition and method of obtaining same by mixing an organic solvent which contains at least 85% by volume parafiinic hydrocarbons and has a boiling point of at least about 300 F. with a cross-linkable resin lacquer. An opaque white coating is obtained by applying the composition to a substrate and curing same thereon.

This application is a division of parent application Ser. No. 781,977, filed Dec. 6, 1968 now abandoned.

BACKGROUND OF THE INVENTION This invention relates to a coating composition. More particularly, it relates to preparation of a lacquer which when applied to a substrate such as wood, metal or the like produces a white opaque coating thereon.

Resin lacquer coatings prepared by use of a portion of the solvent which is compatible with but not completely soluble in the remainder are known. For example, Coney et al. US. Pats. 2,875,164, 3,265,645 and 3,282,- 716 teach employment of a multi-component solvent and involve cellulose ester/ urea formaldehyde lacquers which, when applied to a substrate may be cured thereon by cross-linking to a clear, high-gloss film. It is also known to add pigments to such lacquers to obtain white rather than clear coatings. Such pigments, however, are relatively expensive, and to obtain the desired degree of whiteness usually 8-10 pounds of lacquer are required to coat a ream of 3,000 square feet. Therefore, development of a coating which permits use of lesser amounts thereof than do prior art coatings and which does not require use of pigments to produce opacity, particularly an opacity or whiteness of the degree desired for use on a substrate such as the aluminum foil conventionally used in packaging mints, chewing gum and the like, represents a highly desirable result. By aluminum I mean aluminum and alloys thereof containing at least 50% by weight aluminum.

It is accordingly an object of this invention to provide a coating composition which is basically non-pigmented but which is white or becomes white when applied to an aluminum or like substrate and cured either at room temperature or at an elevated temperature. Another object of this invention is to provide a method for producing an apoque white coating which does not require use of white pigments. A further object of this invention is to provide a substrate coated with a white-colored lacquer. Further objects will be apparent from the description and claims which follow.

SUMMARY OF THE INVENTION In its broader aspects my invention involves mixing a cross-linking catalyst and an organic liquid comprising at least 85% by volume parafiinic hydrocarbons, such as mineral spirits or the like, said liquid having a boiling point of at least about 300 F., with a lacquer in which is dissolved a cross-linkable resin and a crosslinking agent.

I will refer to the added organic liquid mixed with the lacquer as the non-solvent, diluent or dispersing phase since it is not a solvent for the lacquer solvent or the cross-linkable resin and cross-linking agent contained therein. As mentioned hereinabove, it must have a boiling point of at least about 300 F. Preferably its boiling point is above 325 F., and most desirably above 350 F. It may contain up to 5% olefins and up to 14% aromatics.

This organic liquid higher-boiling non-solvent, or diluent, is a material which the lacquer (active) solvent and lacquer solids will tolerate without any substantial precipitation thereof. Also, this organic liquid, non-solvent or diluent used as the dispersing phase according to my invention, by taking longer to evaporate due to its higher boiling point, gives time for the desired opacity to develop. Organic liquids useful according to my invention as this non-solvent ingredient are, for example, odorless naphtha or Stoddard solvents, mineral spirits, and mineral oils which have the required boiling point and paraflinic hydrocarbon content. Illustrative higher-boiling liquids use ful according to my invention are Sohio 3440, Sohio 3454, Shell Oil Company mineral spirits, Sohio Stoddard Solvent 3039 and Sohio Solvent 140. Atlantic Refining Company Atreol 21 mineral oil was also found to be useful in developing the desired opaque white coating. Preferred amount of this non-solvent is from about 12% to about 40% by Weight.

The cross-linkable resin may be a cellulose ester, such as cellulose acetate propionate and cellulose acetate butyrate or an alkyd resin, such as those obtained by condensing and polymerizing phthalic anhydride or other dicarboxylic acid with a polyhydroxy alcohol such as glycerol, modified by fatty acids, drying oils such as linseed, or the like, if desired. Representative cellulose esters useful according to my invention include the propionic and butyric acid esters of cellulose. Particularly useful are those which are soluble in alcohols, e.g., ethyl alcohol, which is a convenient lacquer (active) solvent according to my invention. A representative cellulose acetate butyrate which I have found suitable according to my invention has a butyryl range of about to 50%, a 1- 10% hydroxyl content and a viscosity range of from about 0.1 to seconds. Typical cellulose esters useful in my invention include those ordinarily referred to as halfsecond cellulose acetate butyrate and half-second cellulose acetate propionates and those commonly called alcoholsoluble butyrates and propionates. A typical useful cellulose acetate propionate might have a propionyl content of from about 40 to 55% and a viscosity of from about 0.1 to seconds. Preferred acetyl content for the cellulose esters useful according to my invention is 1-10%.

The cross-linking agent is a compound with which the resin will cross link to form a cured coating. It must be compatible with the cross-linkable resin. Preferred is a. condensation polymer. The condensation polymer may be one formed by condensation of a urea-type compound such as urea, thiourea, cyanamide, guanidine, melamine or the like with a lower aliphatic aldehyde (usually an aldehyde containing from 1 to 4 carbon atoms, and most commonly formaldehyde), or with such an aldehyde and an alcohol, for example, butanol. For example, the urea formaldehyde polymers of the above-mentioned Coney et al. patents may be used as the condensation polymer.

For example, the specific ureas formaldehyde polymer may be dimethylol urea. The urea formaldehyde polymer may be alkylated, for example, such as the butylated urea formaldehyde of above-mentioned Coney et al. U.S. Pat. 3,265,645. Representative urea formaldehyde resins include American Cyanamid Beetle 216-8 supplied at 60% solids in butanol/xylol, Beetle XB-l047 supplied at solids in isobutanol/xylene and Reichold Chemicals Beckamine P-196-60, an alcohol-soluble urea resin furnished at 60% solids. Representative melamine polymers which I have found useful according to my invention include American Cyanamid Cymel 300 and Cymel 301, hexamethoxymethyl melamine resins. Such condensation polymers may be incorporated in the lacquer in unpolymerized, polymerized or partially polymerized form. For convenience I will refer to such a condensation polymer as a urea-formaldehyde or melamine polymer.

When applied to a substrate, for example, wood or aluminum, my lacquer may be cured by air drying or heating to an elevated temperature to accomplish curing by cross-linking of the resin with the cross-linking agent and resultant production of an opaque white coating. The cross-linking agent reacts with reactive groups of the crosslinkable resin, for example, the hydroxy groups of cellulose acetate butyrate or cellulose acetate propionate when the cross-linkable resin used is a cellulose ester. It is believed that curing takes place by evaporation first of the lacquer (active) solvent, that is, the solvent in which the cross-linkable resin and the cross-linking agent are dissolved, which may be called the dispersion phase. At this point the coating appears practically clear and in an initial state of cure wherein some rigidity is possessed but not the hardness of a fully cured lacquer. Then the coating cures completely to a white opaque color upon evaporation of the non-solvent, or diluent, which has a higher boiling point, that is, the above-defined paraffinic hydrocarbon having a boiling point of at least about 300 F. It appears that the non-solvent is dispersed in the lacquer film as minute particles 0.2-1.5 microns in size (diameter) and when the higher-boiling non-solvent is driven off from the partially cured lacquer film, this leaves spherical voids of the same 0.2-1.5 micron size with resultant light scattering at the air-lacquer solids interfaces producing the white-colored opacity.

Preferred concentration of cross-linkable resin and of cross-linking agent is from about 3.3 to about 20% by weight of the resin lacquer without higher-boiling nonsolvent and from about 2 to about 20% by weight of the coating composition with higher-boiling non-solvent.

The solvent for the resin/cross-linking agent lacquer or dispersion phase of my invention I designate as an alcoholtype solvent as ethyl alcohol is a represenative solvent, although this solvent may contain one or more additional similar substances, such as ketones and organic esters, which it is believed help to lessen the gradual increase in viscosity which generally takes place after the composition is made up. The lacquer solvent may contain a high percentage of a lower aliphatic alcohol, for example, the aforementioned ethyl alcohol. Representative components of the lacquer solvent, which may also be called the active solvent, that is, the lower-boiling solvent of the dispersion phase, are methyl ethyl ketone, methyl isobutyl ketone, acetone, ethyl cellusolve, ethyl alcohol, isopropanol, ethyl acetate, n-propyl alcohol, n-butyl alcohol and the like. Mixtures of two or more of the foregoing may be used. For example, any of the solvents or mixtures of solvents for the cross-linkable resin/cross-linking agent may be the predominantly non-aqueous solvents used in above-mentioned Coney et al. U.S. Pats. 2,875,164, 3,282,716 and 3,265,645. The active or lacquer solvent (lower-boiling solvent) preferably has a boiling point of less than about 275 F. Preferred concentration of this lower-boiling or active solvent for the cross-linkable resin and cross-linking agent is from about 6 to about 60% of the coating composition of my invention including the higher-boiling nonsolvent.

The preferred weight ratio for the amount of higherboiling organic liquid or diluent to solids content of the lacquer containing the cross-linkable resin and the crosslinking agent is from about 0.75:1 to about 1.75:1.

A cross-linking catalyst is essential for forming the desired amount of white color or opacity developed upon curing, that is, in cross-linking the resin with the crosslinking agent. Usually an acid catalyst is used. Representative acid catalysts which may be used according to my invention include the preferred catalysts p-toluene sulfonic acid and methane sulfonic acid and sulfuric acid, plus other alkane sulfonic acids, hydrochloric acid, nitric acid, and the like. Other acid catalysts which may be useful include those of Coney et a1. U.S. 3,282,716 referredto above, specifically, methyl, ethyl or propyl sulfonic acids, or a mixed alkane sulfonic acid such as described in U.S.

2,875,164. Preferred amount of catalyst useful according to my invention is from about 0.035 to about 1.7% by weight of the lacquer without the higher-boiling solvent (this percent not including the butyl alcohol or other diluting solvent for the catalyst to give, for example, a 25% solution of catalysts such as sometimes useful) and from about 0.025 to about 2% by weight of the lacquer with higher-boiling point solvent added thereto. Aging the catalyst, for example, by boiling for two hours and then storing at room temperature for a week or two, tends to result in a somewhat more stable coating composition and to prevent premature curing or failure to form the desired amount of white color or opacity.

Conventional plasticizers which may be used in the coating composition of this invention, preferably in amounts up to about 4% by weight of the total composition containing the higher-boiling liquid or diluent, include the preferred triphenyl phosphate and 2-ethyl hexyl diphenyl phosphate, plus chlorinated biphenyl, chlorinated triphenyls, dioctyl phthalate, and the like. Blends of plasticizers may be used, for example, a blend of dioctyl phthalate with a more active plasticizer.

According to my invention there may be used up to about 10% of one or more modifying resins based upon the weight of the coating composition including the diluent. For example, one or more of the following may be used to modify viscosity and improve final toughness and water resistance of the lacquer When coated and cured on a substrate: epoxy resins such as Shell Epon 836, Epon 828 and Epon 1004, which are epichlorhydrin-bisphenol A type polymers ranging from liquid to solid resins and ranging in epoxide values from about to about 1025; phenolic resins such as General Electric Methylon 75108, and polyvinyl butyral resins such as Union Carbide XYI-IL, and the like.

If it is desired to add color to the opaque coating formed by curing of the coating composition according to my invention or to produce an even higher degree of whiteness, dyes and pigments may be added in amounts up to about 12% by weight. Slip agents such as talc, mineral oil, dimethyl silicone polymers, and graphite may also be added in similiar amounts to reduce the coefficient of friction of the surface of the particular substrate coated with the cured coating composition according to my invention.

Small amounts of other conventional additives such as antioxidants may also be used in the coating composition of my invention provided they are compatible with the other ingredients and not reactive in such a way as to destroy the desired opaque white color when it is coated on a substrate.

According to my invention the dispersing phase, that is, the higher-boiling organic liquid, diluent or non-solvent, should be added to the mixture last, preferably just after the addition of the catalyst. It should be mixed with the remaining ingredients sufiiciently to cause the desired droplets to form. If a clear dispersion does not result at first, continued mixing will produce one. That is, there should be enough mixing by stirring, shaking, or the like to disperse any gel which may be formed and to form an almost clear solution.

It is preferred in preparing the coating composition,

cross-linking, that the cross-linking agent be added to the lacquer just before addition of the catalyst and the higher-boiling solvent, which, as just explained, are added last. This will help to prevent premature curing.

If the required cross-linking of the resin with the crosslinking agent is obtained by air curing, usually about 24 to 96 hours are required after application to substrate to obtain a satisfactory degree of whiteness or opacity. When curing is accomplished by heating, a temperature of about 250 F. to 750 F. is preferred. Best development of opacity is at 650-750 F. for from 1-60 seconds.

The coating may be applied by spraying, rolling, brushing or the like. One way is to use a gravure roll and a web containing the coated substrate run at 200-300 ft./ min. directly into an oven at 400750,F. In such a procedure the several steps involved in producing the desired opaque coating are accomplished in rapid succession. First the active solvent is driven off, then the non-solvent or diluent droplets become distributed in the lacquer, with the resin cross-linking with the cross-linking agent and becoming semi-rigid to rigid, and finally the higher boiling non-solvent being driven from its entrapped globular form to leave minute voids which develop the desired whiteness or opacity.

The amount of lacquer applied, when used on foil, is usually about 0.5 to 5 lbs/3,000 sq. ft., preferably 1-3 lbs/3,000 sq. ft., that is, a suflicient amount to result in a coating thickness of about $3 to /2 mil or .00001 to .0005 inch.

The following examples are illustrative of the invention.

Example 1 A formulation containing 31% non-volatile material was made as follows:

Material Weight-Gram Alcohol Soluble Butyrate 13.5 Urea Formaldehyde in Ethyl Alcohol 22.5 Dioctyl Phthalate 3.0 Anhydrous Ethyl Alcohol 60.0 p-Toluene Sulfonic Acid 1.0

The butyrate used was ethyl alcohol-soluble, and the sole lacquer solvent in this example was ethyl alcohol. Curing was effected by reaction of urea formaldehyde with hydroxy groups of the butyrate.

Thirty-one grams of odorless mineral spirits were added to 100 grams of the above lacquer in a bottle. The bottle was then shaken for about 30 minutes on a paint shaker to disperse the mineral spirits in the lacquer. The lacquer was then applied at about two pounds of dry lacquer solids per 3,000 sq. ft. on 1145-0 aluminum foil of about .002 inch in thickness. On drying with a small hand dryer to remove alcohol, an almost transparent coating with very little tackiness was first formed. The coated foil was then placed in a forced-draft oven at 400 F. for 15 seconds to drive off the mineral spirits and complete the cross-linking cure. A highly opaque white coating was produced.

Thin layers of this coating when viewed at 700 magnification with transmitted light showed very small, tightly packed spheres or bubbles. In an electron microscope at 20,000x and 50,000X the bubbles appeared to be almost perfect spheres. The spheres appeared to be in the approximate range of 0.2 to 1.5 microns in diameter. Electron micrographs were made.

The white coating had good adhesion to annealed foil and fair adhesion even after water immersion. It also showed good scuif resistance and did not lose whiteness on applying an over-print lacquer. It did not blacken or lose whiteness when placed in a heat sealer at 280 F. and 30 p.s.i. for 1 second.

Example 2 The following formulation was made and coated on annealed foil, the foil used being toluene-cleaned and consisting of 3003-H19 aluminum alloy:

PART A Material: Pounds Alcohol Soluble Butyrate 6.82 Triphenyl Phosphate (Plasticizer) 1.50 Twenty percent solution of epoxy resin 6.00 Phenolic resin 1.50

Solvent [in parts, 25 MEK (methyl ethyl ketone), 46.2 isopropanol, 28.8 ethyl acetate] 30.30 Odorless mineral spirits 22.0

PART B Example 3 The following formulation was made up and applied to aluminum foil. The butyrate and epoxy resin solutions were mixed separately and allowed to cool to room temperature before use. The B part was added and mixed with the lacquer just before use, the mineral spirits being added last. Addition of the mineral spirits caused a gel formation which was dispersed to form an almost clear solution upon further mixing. The resulting lacquer contained 20.7% solids. Viscosity of the freshly made solution was 23 seconds, No. 2 Zahn cup. The viscosity increased to about 40 seconds over three days. The lacquer was applied on an Inta Roto machine with a 65 line helix roll and a smoother bar to give 2.5 1bs./3,000 sq. ft. on .0035" 1145-0 aluminum foil. The temperature was raised to about 400 F. to develop the desired whiteness. The same composition was also applied at the rate of 1.4 lbs./ 3,000 sq. ft. Application was similar except that no smoother bar was used.

A SOLUTION Pounds Alcohol-soluble butyrate 6.81

Solvent (25.2% MEK+28.8% ethyl acetate-[- 46.0% isopropyl alcoholby wt.) 28.99

B MATERIALS The 'B materials were added to the A solution just before using on the coating machine.

Urea-formaldehyde 13.02 Solvent (25.2% MEK+28.8% ethyl acetate-[- '46L0% isopropyl alcoholby wt.) 8.02 p-Toluene sulfonic acid solution (25% in n-butyl alcohol). (This solution was boiled two hours before use.) .92 Odorless mineral spirits 25.20

Example 4 A coating composition substantially the same as that of Example 3 was prepared except that only 0.8 gram of catalyst and 22.0 grams of mineral spirits (Sohio 3440) were used. Upon evaporation at the higher-boiling temperature required to evaporate the mineral spirits, the small spheres of mineral spirits which were trapped within the lacquer composition were driven off to leave small spherical voids. A white opacity resulted. Sohio 3454 hydrocarbon liquid was then used in place of Sohio 3440 as the higher-boiling non-solvent. Both of these liquids have an initial boiling point above 350 F., and both are straight aliphatic materials with no aromatics. The KB value for both is around 26 or 27. Other higher-boiling non-solvents were also tried, including Shell Oil mineral spirits with a boiling range of 324 to 398 F. and an aromatic content of 16%, Sohio Stoddard solvent 3039 and Sohio solvent 140, with boiling ranges similar to the Shell mineral spirits. Atlantic Refining Company 'Atreol 21 mineral oil was also used with a somewhat lesser degree of whiteness resulting.

Example To determine amounts of higher-boilingorganic liquid which will give the desired whiteness, various amounts of Sohio 3440 mineral spirits were added to a composition substantially the. same as that of Example/4 except i911 the amount of mineral spirits. The mineral spirits were used with 65.28 grams of solution. The, following table shows the degree of whiteness produced after coating and curing. 4

whiteness when applied to aluminum foil and cured thereon.

Weight Percent l Butyric acid ester of cellulose 10.44 Epoxy resin 1183 Phenolic resin 2.30 Plasticizer Urea-formaldehyde resin 1 Catalyst I I Solvent 72.38

I (27.6% solids) j f 1139.09 Mineral spirits (ratio of mineral spirits to solids:

1.35:1) *37.3 grams of mineral spirits added to 100'gran1spt preceding lacquer.

Thebutyrate ester of cellulose, which contained about 1.6% acetyl and about 4.5% hydroxy, was dissolved in solvent. Use of a high speed mixer results in arise in temperature..The solution was allowed to co ol. .Ihenthe epoxy resin was added as a 20% byweight solution.;Tl1en the phenolic resin and plasticizer were added. Then-the urea-formaldehyde resin was added. Just prior;.to, .use,.the

catalyst, 25% p-toluene sulfonic acid in butanol, and

propeller type mixerthe gel disappeared once the active resin solvent was thoroughly mixed with the mineral spiritsQand a clear solution resulted. Y I

The viscosity of the solution at the beginning'was 23 seconds on a No. 2 Zahn cup and rose to about 27 seconds in eight hours.

' This solution may be applied by means of a coating bar, by roto-gravure or by other methods to aluminum foil or other substrates. Air drying results in a white coat ing. Somewhatj,bette'r film "properties may be obtained when curing is done at higher temperatures. A tough solvent resistant andwater resistant high opacity film is obtained when the coating isapplied to .002"-thick annea'led aluminum'foilfand then dried at 450 F. for 15 seconds in a forced-draft oven. I

Example7. v v 10.8 g'ra'msof a 10% solution of Geigy Chemical Corp. Irgacet Scarlet GL dye were added to 100 grams of the solution of Example 6 to produce an opaque scarlet color. The 'Ir'gacet dyes aresolvent soltible"hydroxyazo metal complexes.

" Example 8 7.7 grams of a 10% solution of Ciba Chemical and Dye Co. Solvent-Soluble Red 2B dyewere added to 100 grams of the solution of Example 6 to give an opaque redcolorl' T his dye is also a metal complexof azo compounds. Example '9 10.8 grams of Intercheinical Corp. Molybdate Orange No. 2613 epoxy pigment dispersion were added to 100 grams of the solution of Example 6 to give an opaque orange color. No. 2613 orange consists of molybdate orange dispersed inan epoxy'resin with solvents. The composition is pigment-{ 15% epoxy resin 1001+ 15% I butyl alcohol+ 15% toluol.

Example 10 I 2.8 grams of Interchemical COrpJMidas Gold No. 9604 butyrate chips were added to grams of thesolution off Example 6. When the coating composition was applied to foil and dried an opaque yellowcoa'ting resulted. When used in coatings that producetransparent films this gold pigment disp 'ersion produces'a transparent gold e i '1' f ."E. I V

Midas Gold No.- 9604 contains 45% iron oxide pigment, 45% cellulose acetate butyrate resin and 15% Plasticizer. 7 A 11 I While the invention has been described in terms of preferred embodiments; the claims appended hereto are intended, to encompass all embodiments-which fall within the spiritof the invention. HaVing-thusdescribed my invention andcertain re; ferredembodiments thereof, 1 claim:

A c at n .sqm s ion-whishba m Oi w e applied to a substrate and cured there'onat a tempera; t u r'e of 'a t least about 4.00" aid coating composition nts, 1) cellulose acetate .jr i n t ftirbi fi l resin, said resin having an hydro'xyl eastern etsam 4.5% to 10%, (2) across-linking agent compatible "with said'resin wherein"said crossflinking "agent-is a condensation'polynierof a compound-selectedfrom the group consisting of a "urea compound, thiourea, cyanamide,

guanidiney'andZmelamineWeactedWitII a compound selected from the group .consisting of a 'lower. aliphatic aldehyde, and-.a .loweraliphatic aldehyde. and alcohol,

- (3) a solvent for said resinandsaid cross-linking agent,

.;(4') n, acid ly .selc t it gm t er muprco si 9. :;1*9 n asi alk ne u a s i e s uric acid, hydrochloric acid and nitt'iCfiGidpdapted,for cross linking said resinwith .saidcross-linking agent, and (5) 'aQBf-E P'R i i da abts i b'r ra s-Wi hth lbd a of'said composition to' form gloBtils'there iri, said organic liquid comprising at least 85% by volume parafiinic hydrocarbons zpid having a boiling point of at least about 300 F.

2. A coating composition which forms an opaque color when applied to a substrate and cured thereon at a temperature of at least about 400 F., said coating composition comprising essentially (1) 2 to 20% by weight cellulose ester cross-linkable resin having an hydroxyl content of from 4.5% to 10%, (2) 2 to 20% by weight condensation polymer cross-linking agent comprising a compound selected from the group consisting of a urea compound, and melamine reacted with a compound selected from the group consisting of a lower aliphatic aldehyde, and a lower aliphatic aldehyde and alcohol, (3) 6 to 60% by weight alcohol solvent for said crosslinkable resin and said cross-linking agent, (4) to 4% by weight plasticizer, .025 to 2% by weight acid catalyst selected from the group consisting of p-toluene sulfonic acid, alkane sulfonic acids, sulfuric acid, hydrochloric acid and nitric acid adapted for crosslinking said resin with said cross-linking agent, and (6) 12 to 40% by weight hydrocarbon organic liquid adapted for mixing with the balance of said composition to form globules therein, said organic liquid comprising at least 85% by volume parafiinic hydrocarbons and having a boiling point of at least about 300 F.

3. A coating composition adapted to form an opaque color when applied to a substrate and cured thereon, said coating composition consisting essentially of (1) 2 to 20% by weight cellulose acetate butyrate or cellulose acetate propionate having an hydroxyl content of from 4.5% to (2) 2 to by weight condensation polymer of a compound selected from the group consisting of a urea compound, and melamine reacted with a compound selected from the group consisting of a lower aliphatic aldehyde, and a lower aliphatic aldehyde and alcohol, (3) 6 to by weight solvent for said propionate or butyrate and said condensation polymer, (4) 0 to 4% by weight plasticizer, (5) .025 to 2% by weight acid catalyst selected from the group consisting of p-toluene sulfonic acid, alkane sulfonic acids, sulfuric acid, hydrochloric acid and nitric acid adapted for promoting cross-linking of said butyrate or propionate with said condensation polymer, (6) 12 to 40% by weight hydrocarbon organic liquid adapted for mixing with the balance of said composition to form globules therein, said organic liquid comprising at least 85% by volume paraflinic hydrocarbons and having a boiling point of at least about 300 F., and (7) 0 to 10% by weight modifying resin selected from the group consisting of epoxy resins, phenolic resins and polyvinyl butyral resins.

References Cited UNITED STATES PATENTS 3,020,172 2/ 1962 Mohnhaupt 117--36.7 3,320,089 5/1967 Bourgeois 117-36.7 3,031,328 4/1962 Iarson 1l736.7 2,469,348 5/ 1949 Young et al. 260--15 3,370,025 2/1968 Salo et al. 26015 3,655,591 4/19'72 Seiner 11736.7 3,245,925 4/1966 Watson 260-22 CQ 2,875,164 2/1959 Ball et al. 26015 3,265,645 8/1966 Coney et al. 260-15 FOREIGN PATENTS 1,518,715 3/1968 France l1736.7

WILLIAM H. SHORT, Primary Examiner E. WOODBERRY, Assistant Examiner U 5. Cl. X.R.

ll736.7; 260 2.5 R, 15, 17 R, 22 CQ, EP, 33.6 R, EP, VA, 850 